Title: Development of Sulfonated Carbon Catalyst for Epoxidation of Vernonia Oil
???metadata.dc.contributor.*???: Belay Woldeyes (Prof.)
Gebremedhn, Tekeste
Keywords: Bamboo;Sulfonated carbon catalyst;Vernonia galamensis;Epoxidation;Epoxidized vernonia oil
Issue Date: Jun-2017
Publisher: AAU
Abstract: A biochar-based catalyst was successfully prepared by sulfonation of pyrolysis char with high concentration (>96%) sulphuric acid. Three biochar-based catalysts with pyrolysis support at three different temperatures (400, 450 and 500oC) were prepared and compared for different characteristics of the catalyst. Further investigations on the biochar based catalyst were conducted to determine the effect of preparation protocol on the above properties of the catalyst. Two established preparation techniques (i.e. preparation protocol with ultrasound sonication and preparation protocol with magnetic stirring method) have been utilized to increase the acid density of sulfonic group (SO3H) during sulfonation. The sulfonated catalysts were characterized using the following analyses: bulk density, elemental analysis, total acid density, Fourier Transform InfraRed (FT-IR) spectroscopy, and X-Ray Diffraction (XRD) spectroscopy. The catalyst supported on biochar pyrolysis at 500oC with ultrasound sonication (C-SO3H-500u) resulted in the maximum, sulfur content and total acid density (4.10 mmol/g). Thus, from the prepared catalyst, catalyst prepared at 500oC (C-SO3H-500u) was selected based on the above characterization and thus further evidence on the morphological structure (SEM) and stability (TGA) of the catalyst was performed. The selected (C-SO3H-500u) catalyst was studied for its activity to catalyze Epoxidation of vernonia oil using peroxyformic acid. Design-Expert 7.0.0 three-level-three-factor BBD was applied for experimental design and statistical analysis of results. A total of 15 experiments were conducted at conditions of reaction temperature 65, 75 and 85oC, a molar ratio of hydrogen peroxide to oil 1.5, 2.5 and 3.5 and 2, 4 and 6 %wt of catalyst loading. From the analysis of experimental results, the interaction effects were studied and the optimal epoxidation reaction process conditions, which will maximize the percentage of conversion was found to be 65oC reaction temperature, 2.36:1 molar ratio of hydrogen peroxide to oil and 6 %wt, catalyst loading which gave 51.45% percentage of conversion. The yield of epoxidized vernonia oil was determined by identifying the structure and a composition of vernonia oil, in comparison to epoxidized vernonia oil, using NMR spectroscopy.
Appears in Collections:Thesis - Process Engineering

Files in This Item:
File Description SizeFormat 
Gebremedhn Tekeste.pdf2.65 MBAdobe PDFView/Open
Show full item record

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.